Short Nonwoven Geotextile
Product Description
Short Nonwoven Geotextile
Product Introduction：
Staple geotextile i non-woven fabric machinery with polyester staple fiber as the main raw material,by opening, carding, laying nets,nedlingand other processes produced.
Performance Characteristics:
*High strength, due to the use of plastic fibers, can maintain suficient strength and elongation in wet and dry conditions.
*Corrosion resistance, long-term corrosion resistance in soil and water with different pHlevels.
*Good water permeability, there is a gap between the fibers, so it has good water seepage performance.
*Good resistance to microorganisms, insects are not damaged.
*Convenient construction, because the material is light and soft, it is convenient for transportation, laying and construction.
*Light weight, low cost, corrosion resistance,with reverse filtration, drainage, isolation, enhancement and other benign properties.
Technical Indicators:
Technical specifications of staple fiber needled nonwoven geotextiles (GB/T 17638-1998):
| Item | Unit | specification | ||||||||||
| 100 | 150 | 200 | 250 | 300 | 350 | 400 | 450 | 500 | 600 | 800 | ||
| Weight variation | % | -8 | -8 | -8 | -8 | -7 | -7 | -7 | -7 | -6 | -6 | -6 |
| thickness | mm | 0.9 | 1.3 | 1.7 | 2.1 | 2.4 | 2.7 | 3.0 | 3.3 | 3.6 | 4.1 | 5.0 |
| width variation | % | -0.5 | ||||||||||
| Breaking strength(MD/TD) | kN/m | ≥2.5 | ≥4.5 | ≥6.5 | ≥8 | ≥9.5 | ≥11 | ≥12.5 | ≥14 | ≥16 | ≥19 | ≥25 |
| Elongation at break | % | 25~100 | ||||||||||
| CBR Mullen Burst Strength | kN/m | ≥0.3 | ≥0.6 | ≥0.9 | ≥1.2 | ≥1.5 | ≥1.8 | ≥2.1 | ≥2.4 | ≥2.7 | ≥3.2 | ≥4 |
| Tear Strengh(MD/TD) | kN/m | ≥0.08 | ≥0.12 | ≥0.16 | ≥0.2 | ≥0.24 | ≥0.28 | ≥0.33 | ≥0.38 | ≥0.42 | ≥0.46 | ≥0.6 |
| Sieve size | / | 0.07~0.2 | ||||||||||
| Vertical permeability coefficient | / | K×(10-1~10-3) | ||||||||||
Technical specifications of staple fiber needled nonwoven geotextiles(GB/T 17638-2017):
| Item | Unit | Nominal breaking strength(kN/m) | ||||||||
| 3 | 5 | 8 | 10 15 | 20 | 25 | 30 | 40 | |||
| Breaking strength(MD/TD) | kN/m | ≥3 | ≥5 | ≥8 | ≥10 | ≥15 | ≥20 | ≥25 | ≥30 | ≥40 |
| Correspondling elongation of Nominalfracture strength | % | 20~100 | ||||||||
| bursting strength | kN/m | ≥0.6 | ≥1 | ≥1.4 | ≥1.8 | ≥2.5 | ≥3.2 | ≥4 | ≥5.5 | ≥7 |
| Tear Strengh(MD/TD) | kN/m | ≥0.1 | ≥0.15 | ≥0.2 | ≥0.25 | ≥0.4 | ≥0.5 | ≥0.65 | ≥0.8 | ≥1 |
| Sleve size O90(O₉₅) | mm | 0.07~0.20 | ||||||||
| Vertical permeabiltycoficent | cm/s | K×(10⊃1;~10⊃3;)： K=1.0-9.9 | ||||||||
| Width deviation rate | % | -0.5 | ||||||||
| devation rate of mass per unit area | % | ±5 | ||||||||
| Thickness deviation rate | % | ±10 | ||||||||
| Acid-base resistance (strong retention) | % | ≥80 | ||||||||
| Antioxidant properties(strong ratention) | % | ≥80 | ||||||||
| Uv resistance (strong retention) | % | ≥80 | ||||||||